31. An In-Vitro Analysis of Microleakage of Self-Adhesive Fissure Sealant vs. Conventional and GIC Fissure Sealants.
Gorseta K1, Borzabadi-Farahani A2, Vrazic T3, Glavina D4.
Author information:
1. Department of Pediatric and Preventive Dentistry, School of Dental Medicine, University of Zagreb, Gunduliceva 5, 10 000 Zagreb, Croatia. kgorseta@sfzg.hr.
2. Department of Clinical Sciences and Translational Medicine, University of Rome Tor Vergata, 00183 Rome, Italy. faraortho@yahoo.com.
3. Private Practice, Varazdin 42000, Croatia. vrazictara@gmail.com.
4. Department of Pediatric and Preventive Dentistry, School of Dental Medicine, University of Zagreb, Gunduliceva 5, 10 000 Zagreb, Croatia. glavina@sfzg.hr.
Abstract
BACKGROUND:
The microleakage of a self-adhesive composite, a glass ionomer fissure sealant and a conventional resin-based fissure sealant were compared.
MATERIALS AND METHODS:
Fifty intact human molars with well-delineated pits and fissures were used and divided into 5 groups (n = 10). Group 1 specimens were etched (37% phosphoric acid) and sealed with conventional resin-based sealant (Helioseal F, Ivoclar Vivadent). Both Group 2 and 3 specimens were sealed with self-adhesive composite (Constic, DMG), but in Group 3, specimens were also etched (37% phosphoric acid). In Groups 4 and 5, specimens were sealed with a GIC sealant (Equia Fill, GC Company), but Group 5 was also exposed to thermo-light curing (TLC) with a LED polymerization unit (60 s). Subsequently, specimens were thermocycled (1800 cycles, dwelling time of 10 s), immersed in 50% silver nitrate solution (45 min), placed in a photo-developing solution (Kodak) under a lamp (120 W, 6 h), and cut into 3⁻4 slices. Marginal leakage (dye penetration depth) was evaluated under a light microscope and the worst score of each specimen was recorded (0⁻3).
RESULTS:
Constic showed the lowest microleakage (Constic: 80% scored 0 or 1), followed by Helioseal (30% scored 0 or 1) (p = 0.037). Microleakage in groups sealed with Constic (with and without etching) were not different (p = 0.473). The quality of seal deteriorated after etching when Constic was used. However, TLC improved the seal when GIC sealant was used (p = 0.016) and also in comparison to Helioseal (p = 0.004). The TLC GIC sealant (Equia Fill, 90% scored 0 or 1) performed well, similar to self-adhesive composite (Constic, 80% scored 0 or 1) (p = 0.206).
CONCLUSION:
The present findings suggest that the self-adhesive sealant and the GIC sealant that were exposed to TLC had comparable sealing ability and superior sealing characteristics compared to the conventional resin-based sealant. A long-term clinical trial is needed to assess the intra-oral performance.
PMID: 30925796